A4-70 A4-80 and A4-100 High Strength Screws

Q: I have difficulties getting A4-70 A4-80 and A4-100 screws in small sizes (M4, M5 and M6). Can you suggest suitable material alternatives?

A: A4 (A4 (1.4401 / 1.4404) is an excellent material for high strength bolts. A4-70 and higher strength screws in small sizes (up to M8) are not standard products. The reason is that A4 (AISI 316) stainless steel is a austenitic material. Therefore, the only way gain high
strength fasteners (with a tensile strength of 700 MPA (A4-70), 800 Mpa (A4-80) or higher is by hardening of the material. The hardening for larger sizes (M10 and up) is obtained during the cold heading of the screws. For smaller screws however, only a tensile strength in the range of 500 MPA (equal to A4-50) or strength class 5.x is typically obtained during production.

It is possible to manufacture A4-70, A4-80 or A4-100 in small sizes by machining those from full hard material (i.e machining a hardened bar) . This is a difficult process as the pre-hardened material can be fairly brittle – which can make small A4 bolts in these sizes quite expensive.

The alternative may be to go for Duplex screws. Machined Duplex screws will have a tensile strength of min (113 ksi / 780 MPA) if machined and can replace A4-70. For higher strength requirements, you should consider titanium grade 5 screws which have a tensile strength of Min 138 ksi / 950 MPA corresponding to A4-80 or A4-90. Replacement of A4-100 is best done by a precipitation hardened material like 17-4PH or Inconel 718 bolts.

The corrosion resistance of Duplex stainless steel, titanium grade 5 and Inconel 718 are
all better than A4. The A4 has PREN numbers in the range 23-28, whereas Duplex is above 30. The 17-4PH material contains slight lower amount of chromium compared to A4 so the pitting resistance may also be lower.

This entry was posted in Application, FAQs, High Strength, Specialty Metal Fasteners, Technical Questions and tagged , , , , , , , , , , , , , , , , . Bookmark the permalink.