Tag Archives: Monel

Q:  I’m running a chemical cleaning process on stainless steel to remove the oxides and to enrich the chromium depleted areas again surface. It’s an acid pickling process, where mixtures of hydrofluoric acid (HF) and nitric acid (HNO3) are used. I’ve tried Hastelloy C276 bolting on my tanks because I thought … Continue reading

Posted in Application, Corrosion Resistance, FAQs, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , , , , , , , | Leave a comment

Q: I have a high strength application that requires resistance to damp salt air and occasional sea splash, I’m using Monel 400 but it’s not holding up the the 75ksi of yield I need. Lots of broken bolts? Is is corrosion or  strength? Thoughts? A: Your issue isn’t the corrosion. … Continue reading

Posted in Application, Corrosion Resistance, FAQs, High Strength, Material, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , , , , , | Leave a comment

Q: Is AL6XN a steel or nickel alloy? Trying to figure out if it would perform as well as Monel in seawater. A: To answer your first question, AL6XN bolts are actually both a nickel and a steel alloy. AL6XN is often described as a high nickel content stainless alloy. Though … Continue reading

Posted in Application, Corrosion Resistance, FAQs, Material, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , , , , , , , , | Leave a comment

Nickel alloys are a special class of metals containing high levels of nickel (often greater than 20%). They play a key role in industry for their unique combination of high strength, corrosion resistance to harsh acids (like hydrochloric and sulfuric) and high temperature stability. This two-part newsletter will help summarize the distinct benefits of the … Continue reading

Posted in Application, Blog, Corrosion Resistance, Material, Specialty Metal Fasteners | Tagged , , , , , , , , , , , , , , , , | Leave a comment

Q: I need to attach an LNG cryogenic pump and need to make sure I use a material that can withstand temperatures of –120 °F as well as don’t embrittle when fluctuating back to room temperature. Any suggestions? A:  Monel K500 is a common choice for  cyrogenic fasteners. It can … Continue reading

Posted in Application, FAQs, High Strength, High Temperature Resistance, Specialty Metal Fasteners, Technical Questions, Uncategorized | Tagged , , , , , , | Leave a comment

Q: I have a salt water environment with high velocities and a lot of debris including sand, dirt and particles. Because of the amount of debris, I’m concerned about what material would work best. A: Both Monel and Titanium can be good choices in this situation. Both perform extremely well … Continue reading

Posted in Application, Corrosion Resistance, Specialty Metal Fasteners | Tagged , , , , , , , , , , , , , | Leave a comment

Q: I’m using hydrogen fluoride used in a manufacturing process to make refrigerants. I know it’s very corrosive and have tried both hastelloy and inconel fasteners, which I thought were super corrosion resistant. What am I doing wrong because the acid is still eating them? Should I try Tantalum? A: … Continue reading

Posted in Corrosion Resistance, FAQs, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , , , , | Leave a comment

inconel-monel-chart-copyThey rhyme, are both used in extreme environments, and are both nickel metal alloys, but Monel and Inconel are actually very different. But how? Let’s start with basic chemistry. Monel is a nickel-copper alloy and Inconel is a nickel-chromium alloy. So what does that mean for your extreme application? We … Continue reading

Posted in Application, Blog, Corrosion Resistance, High Strength, High Temperature Resistance, Specialty Metal Fasteners | Tagged , , , , , , , , , , , | 1 Comment

Q: I’m currently using Monel 400 hex head bolts in salt water. Should I be using K500? What’s the difference? A: Basically, Monel K500 is a precipitation hardened version of Monel 400. This means the material goes through a heat treating process that changes the alloy’s structural matrix to increase its tensile and … Continue reading

Posted in Corrosion Resistance, FAQs, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , | Leave a comment

Q: I have a seawater application where the water can be stagnant or polluted. Is Monel bolts the best choice? A: For stagnant seawater application we would usually suggest Titanium over Monel fasteners. Although Monel is very resistant to saltwater, it can experience pitting corrosion in stagnant water situations. There have … Continue reading

Posted in Corrosion Resistance, FAQs, Specialty Metal Fasteners, Technical Questions | Tagged , , , | Leave a comment

So you’ve heard the term, but what is it? Technically, it is a method in which an alloy’s structural matrix is altered on an atomic level by using temperature change to enhance the material’s mechanical properties – increasing the yield and tensile strength. Simply, it is a way to further strengthen a material. It is … Continue reading

Posted in Blog | Tagged , , , , , , , , , , , , , , , , , , , , | Leave a comment