Tag Archives: Inconel

Q: I’m in need of a high strength fastener that can withstand moderate concentrations of hydrochloric acid (HCl) 25%? Can I use Hastelloy Bolts? I need a bolt that can handle a yield of about 100ksi and temperatures around 100F. A: Hastelloy bolts are definitely ideal in this concentration of … Continue reading

Posted in Application, Corrosion Resistance, FAQs, Material, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , | Leave a comment

Q: I’m operating a FGD (Flue Gas Desulphurization) plant and am experiencing some mild corrosion on my scrubber bolting. I’m currently using Incoloy 825 bolts. It’s mild corrosion but non-the-less I’d like to have it cleared up before I get additional issues. Any suggestions? A: Since scrubber liquids and gases … Continue reading

Posted in Application, Corrosion Resistance, FAQs, Material, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , , , , , , | Leave a comment

Q:  I am considering using Inconel 718 fasteners with a Monel K-500 flange in seawater. I’m concered as Inconel is the more anodic of the two and is also has a smaller surface area. Would this cause galvanic corrosion? A:  This is a great question. In this case if you plan … Continue reading

Posted in Application, Corrosion Resistance, FAQs, Material, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , , , , | Leave a comment

Q: My customer is having an issue with his stainless steel fastener bending. They are being used in a high-heat application running at approximately 1600F. Is this normal? Any ideas? A: This is definitely expected at these temperatures. If temperature and strength are you main focus, I would suggest either … Continue reading

Posted in Application, FAQs, High Strength, High Temperature Resistance, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , | Leave a comment

Q: I have a high temperature application which is exposed to sulfur and chloride gasses. We’re operating at between 1200° and 1400°F. Any suggestions on a bolt material to consider? A: To deal with both sulfuric/chloride atmospheres as well as high temperatures, you may want to consider Incoloy 800HT bolts … Continue reading

Posted in Application, Corrosion Resistance, FAQs, High Temperature Resistance, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , , , , , , | Leave a comment

Q: Inconel 625 and Hastelloy C276 bolts seem to have similar Nickel content. Does this mean these fasteners will perform the same in a corrosive environment? A: Inconel 625 and Hastelloy C276 bolts do offer similar corrosion resistance but Hastelloy C276 has a slight edge in many acidic environements, especially … Continue reading

Posted in Application, Corrosion Resistance, FAQs, Material, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , , , , , , , , , | Leave a comment

Q: I’m working with boiling sulfuric acid and tried Alloy 20 for some of my bolting but am having corrosion. I’m confused as I thought that is what they are best for. Any suggestions. A: You are right Alloy 20 does typically perform very well in sulfuric acid and even … Continue reading

Posted in Application, FAQs, Material, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , , , , , , , | Leave a comment

Q: I need a material that will be suitable for oil and gas use. Submersion in hydrogen sulfide, carbon dioxide, hydrocarbons, salt water at temperatures up to 325F. Crevice corrosion has been a factor. Also need 170ksi min tensile strength. Plus we’d like to torque a 3/8-24 fastener to 50 … Continue reading

Posted in Application, Corrosion Resistance, FAQs, High Strength, Specialty Metal Fasteners, Technical Questions, Uncategorized | Tagged , , , , , , , , | Leave a comment

Q: We are running a steel pickling process are considering switching from a sulfuric acid process to hydrochloric acid. Our system currently uses Inconel 625 bolting. With this be sufficient? A: Inconel 625 is a good material for acid corrosion but for large system of hydrochloric acid, especially with the … Continue reading

Posted in Application, Corrosion Resistance, FAQs, Material, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , , , | Leave a comment

Q: I’m using zirconium fasteners in a sulfuric acid process but they are showing corrosion. I’m not sure why as I’m well below boiling and only using 40% concentration. There may be some downstream contaminants, but not much. Any ideas? A: It is most likely the contaminants that are causing … Continue reading

Posted in Application, Corrosion Resistance, FAQs, High Temperature Resistance, Material, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , , , , , , , , , , , , | Leave a comment

Q: I’m working on a on a geothermal energy drilling project. Carbon steel we’re currently using to bolt drilling components is failing from corrosion. We have corrosive an environment with high levels of sulfur and salt, as well as temperatures to 260C. Any suggestions? A: Super Duplex 2507 is often used … Continue reading

Posted in Application, Corrosion Resistance, FAQs, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , , , , , , , | Leave a comment

q: What bolting material should be used with Inconel 625 flanges? We used ASTM A193 Gr B7 however noticing some corrosion issues. A: This is a very common problem but to answer it accurately, it depends on the environment that your flanges see and also to a certain extent what … Continue reading

Posted in Application, Corrosion Resistance, FAQs, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , , | Leave a comment

inconel-monel-chart-copyThey rhyme, are both used in extreme environments, and are both nickel metal alloys, but Monel and Inconel are actually very different. But how? Let’s start with basic chemistry. Monel is a nickel-copper alloy and Inconel is a nickel-chromium alloy. So what does that mean for your extreme application? We … Continue reading

Posted in Application, Blog, Corrosion Resistance, High Strength, High Temperature Resistance, Specialty Metal Fasteners | Tagged , , , , , , , , , , , | 1 Comment

Inconel fasteners are commonly used for extreme environments and come in various “flavors” depending on the needs of the application. This brief paper will give you a quick comparison of the two most popular grades, Inconel 625 and Inconel 718 to help you choose the best material.

Posted in Blog | Tagged , , , , , , , , , , , , | 1 Comment

Q: Can dissimilar (also called galvanic) corrosion occurs between Inconel bolts and regular carbon steel? A:   Anytime you have dissimilar materials you have the potential for galvanic corrosion.  For this to happen the materials need to be wet or in some kind of solution. If they are dry it’s … Continue reading

Posted in Corrosion Resistance, FAQs, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , | Leave a comment

lock-nut-chartA lock nut resists loosening from vibrations and torque. Specialty material lock nuts offer the ideal solution to many extreme applications environments. They combine the unique properties of specialty materials, with the secure locking feature of a lock nut to prevent failures in the field.

Posted in Blog | Tagged , , , , , , , , , , , , | 5 Comments

So you’ve heard the term, but what is it? Technically, it is a method in which an alloy’s structural matrix is altered on an atomic level by using temperature change to enhance the material’s mechanical properties – increasing the yield and tensile strength. Simply, it is a way to further strengthen a material. It is … Continue reading

Posted in Blog | Tagged , , , , , , , , , , , , , , , , , , , , | Leave a comment